Dymax Multi-Cure 9001-E-V3.5 UV Curing Encapsulant Clear 170 mL Cartridge

Part number: 9001-E-V3.5 170ML CARTRIDG Manufacturer SKU: 9001-E-V3.5/160CRT
Dymax Multi-Cure 9001-E-V3.5 UV Curing Encapsulant Clear 170 mL Cartridge
Quantity Price
1 $114.78 ($11.48 each) 114.780000000 USD New Available 9001-E-V3.5 170ML CARTRIDG
2 $88.38 ($8.84 each) 88.380000000 USD New Available 9001-E-V3.5 170ML CARTRIDG
3+ $82.07 ($8.21 each) 82.070000000 USD New Available 9001-E-V3.5 170ML CARTRIDG
Sold as a pack (10/pk).
Usually Ships in 2-3 Business Weeks. NON-RETURNABLE.
  • A Made in the USA

DYMAX 9001-E-V3 Series Encapsulant Clear is a one component, UV light and heat curing, acrylated urethane that is used for bonding electronic devices, print circuit boards, glass, multi-chip modules, chip-on-flex, and chip-on-board applications. It offers flexibility, good electrical properties, and resistance to thermal cycle and moisture. 170 mL Cartridge.

DYMAX 9001-E-V3 Series Encapsulant Clear is a one component, UV light and heat curing, acrylated urethane that is used for bonding electronic devices, print circuit boards, glass, multi-chip modules, chip-on-flex, and chip-on-board applications. It offers flexibility, good electrical properties, and resistance to thermal cycle and moisture. 170 mL Cartridge.
Typical Use: Multi-Cure 9001-E-V3 series encapsulants display excellent adhesion to PC boards and electronic components and are especially well suited for chip on board, chip on flex, and multi-chip modules.
Brand: Multi-Cure
Chemical Composition: Acrylated urethane
Color: Clear
Components: 1 part
Cure System: UV
Cure Time: Actual cure time typically is 3 to 5 times fixture time.
Dielectric Strength: 500 kV/mm
Elongation: 150% @ break
Flash Point: 101 °C
Hardness: 45 D
Service Temperature: -54 to 150 °C
Tensile Strength: 750 psi @ break
Viscosity: 17,000
Volume Resistivity: 555 x 10^12 ohm-cm

 