Dow SYLGARD™ 184 Silicone Curing Agent Clear 20.4 kg Pail

Part number: 184 CURING AGENT 20.4KG PL Manufacturer SKU: 2120925
Dow SYLGARD™ 184 Silicone Curing Agent Clear 20.4 kg Pail
Quantity Price
1 $3,107.37 3107.370000000 USD New Limited Availability 184 CURING AGENT 20.4KG PL
2 $2,838.06 2838.060000000 USD New Limited Availability 184 CURING AGENT 20.4KG PL
3+ $2,775.92 2775.920000000 USD New Limited Availability 184 CURING AGENT 20.4KG PL
Usually Ships in 7-8 Business Weeks. NON-RETURNABLE.
  • A Made in the USA

Dow SYLGARD™ 184 Clear is a two component, flowable, room temperature and heat cure silicone curing agent with good dielectric properties and flame resistance. Curing agent only. It is to be used with Dow SYLGARD™ 184 Base to form a flexible, encapsulant that is used to protect electrical applications. 20.4 kg Pail.

<p>Dow&nbsp;SYLGARD™ 184 Clear is a two component, flowable, room temperature and heat cure silicone curing agent with good dielectric properties and flame resistance. Curing agent only. It is to be used with Dow SYLGARD™ 184 Base to form a flexible, encapsulant that is used to protect electrical applications. 20.4 kg Pail.</p>
Typical Use: Typically used for LED lighting encapsulation, power supplies, connectors, sensors, industrial controls, transformers, amplifiers, high voltage resistor packs, relays, solar cells and adhesive handling beam lead integrated circuits during processing.
Brand: SYLGARD
Chemical Composition: Silicone
Color: Clear
Components: 2 part
Cure System: Room Temperature/Heat
Cure Time: 48h @ 25 °C; 35min @ 100 ºC; 20min @ 125 ºC; 10min @ 150 ºC
Dielectric Strength: 19 kV/mm
Flash Point: > 101.1 ºC
Mix Ratio: 10:1
Service Temperature: -45 to 200 °C
Specific Gravity: 1.03
Tensile Strength: 980 psi
Thermal Conductivity: 0.27 W/mK
Viscosity: Mixed: 3500
Volume Resistivity: 2.9 x 10^14 ohm-cm
Working Time: 1.5 @ 25 °C

 